The fast sintering furnace used silicon carbide as heating rods, and the sintering time was reduced to 1 hour. In contrast, the slow sintering furnace, which uses silicon molybdenum as heating rods, has a lifespan of 500 times its use.
Thanks for the heating rods that were graded. The crucible is being upgraded at the same time. The fast sintering furnace used a 60mm crucible, loading 20 units of dentures, once sintering. And the slow furnace used a 3-layer 100mm crucible, so that once sintering can be loaded up to 150 dentures.
Crucible size: 60mm*/90mm*2/100mm*3
Crucible layer: 1/2/3 layers
Crucible lifespan: 100 times used
The TS Series Zirconia Sintering Furnace is specifically engineered for dental. Allowing zirconia restorations to be placed directly without manual calibration temperature while guaranteeing zero metal ion contamination to preserve the final aesthetic and biocompatibility of the prosthesis. Furthermore, to proactively safeguard the aesthetic integrity of every restoration and prevent common surface defects, the system incorporates proprietary Zirconia Pre-Drying Technology, which automatically eliminates residual moisture before the sintering cycle. Finally, overall operational reliability is significantly enhanced by an advanced low-voltage drive, a measure implemented to reduce the thermal load on the heating elements and thereby maximize their service life and system uptime.
|
|
|
|
|
|---|---|---|---|
| Model | T1S | T2S | T3S |
| Voltage | 110-120V | 110-240V | 120V |
| Power | 2800W | 1200W | 2800W |
| Max Temperature | 1550°C | 1530°C | 1650°C |
| Heating Rod | Silicon Carbon*5 | Silicon Carbon*4 | Silicon Molybdenum*4 |
| Rod Lifespan | 300 Times | 300 Times | 500 Times |
| Heating Rate | 200°C/min | 200°C/min | 100°C/min |
| Capacity | 80units | 10-20units | 150units |
| Crucible | 90mm*2 | 60mm*1 | 100mm*3 |
| Crucible Lifespan | 100 Times | 100 Times | 100 Times |
| Sintering Model | Fast Model | Fast Model | Standard |
| Sintering Time | 1 Hour | 1 Hour | 4 Hours |
| Languages | EN/ES/RU | EN/ES/RU | EN/ES/RU |