| Size | 95mm, 98mm, AG |
|---|---|
| Thickness | 10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm |
| Color | A1, A2, A3, A3.5, A4, B1, B2, B3, B4, BL1, BL2, BL3, BL4, C1, C2, C3, C4, D2, D3, D4 |
The 3D PRO Zirconia Block emerges as an exceptionally economical choice, integrating a sophisticated 5-layer multilayer system. This structure achieves smooth, biomimetic transitions across optical and physical properties. It features a significant flexural strength gradient, engineered from 800 MPa to a robust 1200 MPa, spanning characteristics typically associated with aesthetic formulations (akin to 4Y-TZP) through to high-strength materials required for load-bearing areas (similar to 3Y-TZP). Concurrently, its translucency subtly shifts from 43% to 49%, ensuring reliable aesthetic outcomes. Fabricated from premium 100% Sinocera raw material, 3D PRO provides extensive clinical utility, suitable for full-contour crowns (anterior and posterior), veneers, inlays/onlays, abutments, and multi-unit bridgework, offering a versatile and value-driven option for diverse restorative needs.
Unlock the future of restorative dentistry with ZirArt 3D Series, the pioneering products from the LODDEN ZirArt Series.
LODDEN Offers high flexibility in ordering, choose the exact size needed for each specific restoration, minimized waste directly translates to reduced denture CAM material costs.
ZirArt 3D PRO Rapid is now a viable, high-quality solution for Chairside Restorations, reducing patient wait times.
| Crown Thickness≤0.5mm | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 45 | 30 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1500 | 25 | 8 |
| Step 4 | 1500 | 1500 | 85 | 0 |
| Step 5 | 1500 | 20 | / | Natureal Cooling |
| Crown Thickness≥0.5mm | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 45 | 30 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1500 | 25 | 8 |
| Step 4 | 1500 | 1500 | 120 | 0 |
| Step 5 | 1500 | 20 | / | Natureal Cooling |
| Long Bridge, Implent Brown, Full Arch | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 65 | 20 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1500 | 30 | 7 |
| Step 4 | 1500 | 1500 | 120 | 0 |
| Step 5 | 1500 | 20 | / | Natureal Cooling |
| 1-3 Unit Bridges | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1100 | 10 | 110 |
| Step 2 | 1100 | 1550 | 60 | 7.5 |
| Step 3 | 1550 | 1500 | 30 | 0 |
| Step 4 | 1550 | 800 | 20 | -37.5 |
| Crown Thickness≤0.5mmh | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 45 | 30 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1530 | 30 | 8 |
| Step 4 | 1530 | 1530 | 85 | 0 |
| Step 5 | 1530 | 20 | / | Natureal Cooling |
| Crown Thickness≥0.5mmh | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 45 | 30 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1530 | 30 | 8 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 20 | / | Natureal Cooling |
| Long Bridge, Implent Brown, Full Arch | ||||
|---|---|---|---|---|
| Sintering Step | Start Temperature(°C) | End Temperature(°C) | Time(Min) | Rate(°C/min) |
| Step 1 | 20 | 1300 | 65 | 20 |
| Step 2 | 1300 | 1300 | 20 | 0 |
| Step 3 | 1300 | 1530 | 35 | 7 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 20 | / | Natureal Cooling |